fracture toughness; MgAl2O4; MgO; modulus; refractories; strength; thermal shock; work of fracture
Microstructural changes, as a consequence of the thermal expansion mismatch between magnesia and spinel phases, and fracture behaviour of magnesia and spinel composites have been investigated as a function of spinel content (10, 20, 30 wt.%). Fracture surfaces of magnesia showed mostly transgranular fracture; for the composites, however, the amount of intergranular fracture increased with increasing spinel content. This change in fracture behaviour is thought to be the main reason for the increase in the work of fracture, gamma(WOF). The 30% spinel composite was found to exhibit both the greatest resistance to crack propagation, and the greatest resistance to thermal shock damage, with the highest retained strength after quenching. (C) 2003 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据