期刊
APPLIED SURFACE SCIENCE
卷 311, 期 -, 页码 593-601出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.apsusc.2014.05.113
关键词
PET fabric; Carbon nanotube; Plasma treatment; Microwave shielding performance
类别
资金
- Islamic Azad University, Birjand branch
Four different procedures were conducted to load amine functionalized multiwall carbon nanotube (NH2-MWCNT) onto poly (ethylene terephthalate) (PET) fabric surface to obtain a microwave shielding sample. Plasma treated fabric which was subsequently coated with NH2-MWCNT in the presence of acrylic acid was chosen as the best sample. Surface changes in the PET fabrics were investigated by X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM). Wide-angle X-ray diffraction was used to study the crystalline structure of the PET fabric. The microwave shielding performance of the PET fabrics in term of reflection loss was determined using a network analyzer at X-band (8.2-12.4 GHz). The XPS results revealed that the carbon atomic percentage decreased while the oxygen atomic percentage increased when the fabric was plasma treated and coated with NH2-MWCNT. The SEM images showed that the NH2-MWCNTs were homogenously dispersed and individually separated in the surface of fabric. Moreover, the structural studies showed that the crystalline region of the fabrics was not affected by NH2-MWCNT and plasma treatment. The best microwave absorbing properties were obtained from the plasma treated fabric which was then coated with 10% NH2-MWCNT in the presence of acrylic acid. It showed a minimum reflection loss of similar to-18.2 dB about 11 GHz. Proper attachments of NH2-MWCNT on the PET fabric surface was explained in the suggested mechanism in which hydrogen bonding and amide linkage are responsible for the achievement of microwave shielding properties with high durability. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据