Bismuth sulfide; Thin films; Chemical deposition; Plasma treatment
类别
资金
- LYFYCS-CONACYT [123122]
- CONACYT [128714]
- DGAPA-UNAM
As-deposited bismuth sulfide (Bi2S3) thin films prepared by chemical bath deposition technique were treated with thermal annealed in air atmosphere and argon AC plasma. The as-deposited, thermally annealing and plasma treatment Bi2S3 thin films have been characterized by X-ray diffraction (XRD) analysis, atomic force microscopy analysis (AFM), transmission, specular reflectance and electrical measurements. The structural, morphological, optical and electrical properties of the films are compared. The XRD analysis showed that both post-deposition treatments, transform the thin films from amorphous to a crystalline phase. The atomic force microscopy (AFM) measurement showed a reduction of roughness for the films treated in plasma. The energy band gap value of the as-prepared film was E-g = 1.61 eV, while for the film thermally annealed was E-g = 1.60 eV and E-g = 1.56 eV for film treated with Plasma. The electrical conductivity under illumination of the as-prepared films was 3.6 x 10(-5) (Omega cm)(-1), whereas the conductivity value for the thermally annealed films was 2.0 X 10(-3) (Omega cm)(-1) and for the plasma treated films the electrical conductivity increases up to 7.7 x 10(-2) (Omega cm)(-1). (C) 2014 Published by Elsevier B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据