A large pulsed electron beam (LPEB) was used to modify the surface properties of a poly( methyl methacrylate) (PMMA) sample. Translucent PMMA samples were fabricated using a conventional milling process. Then, the surface was irradiated with an energy density of 2 to 4 J/cm(2) by a large electron beam, 60 mm in size. Surface property characterization of the irradiated PMMA samples was performed using an ultraviolet-visible-near infrared (UV-vis-NIR) spectrophotometer, atomic force microscopy, a form tracer, and drop-shape analysis and compared with the non-irradiated surface. It was observed that the visible light transmission of the prepared PMMA sample was enhanced by 40%. The surface roughness of the PMMA sample after irradiation was also reduced by 30%, compared with the baseline case with no irradiation. Additionally, the water contact angle increased as the number of LPEB shots increased. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据