APPLIED SURFACE SCIENCE
卷 279, 期 -, 页码 189-196出版社
ELSEVIER
DOI: 10.1016/j.apsusc.2013.04.068
关键词
Self-lubricating; CrAlN/VN; Multilayer coatings; Mechanical performance; Magnetron sputtering
类别
资金
- National Natural Science Foundation of China [51202035]
- National Science Council, Taiwan [NSC 100-2221-E-131-008-MY3]
- CISRI [11020990A]
Vanadium nitride (VN) is easily oxidized to form vanadium oxides and becomes lubricious under stress. CrAlN is hard thus CrAlN/VN multilayer coatings render both hardness and lubricious properties attractive in dry machining of soft metals. This study investigates the effect of multi-layering on the coating's mechanical and tribological properties at room temperature. The CrAlN/VN multilayer coatings are deposited on cemented tungsten carbide and Si wafer (100) substrates in an in-line magnetron sputtering system. A period contains one layer of CrAlN plus one adjacent layer of VN. The period thickness varies roughly from 3 nm to 30 nm; the total number of the periods varies from 30 to 300. X-ray diffractometry, scanning electron microscopy, transmission electron microscopy, X-ray photoelectron spectroscopy and electron probe micro-analyzer are employed to characterize the microstructures and chemistry. Nanoindentation and ball-on-disk wear test are used in mechanical and tribological studies. The CrAlN/VN multilayer coatings have good lubricant property with lowest coefficient of friction of 0.26. At the period thickness of 20 nm, the multilayer coatings obtained the best mechanical properties (hardness of 32.4 GPa, elastic modulus of 375 GPa, minimum wear rate of 1.1 x 10(-7) mm(3)/Nm). (C) 2013 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据