APPLIED SURFACE SCIENCE
卷 282, 期 -, 页码 217-225出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.apsusc.2013.05.105
关键词
MCM-41; Surface area; Surface acidity; Hydroquinone diacetate
12-molybdophosphoric acid (PMA) was supported on mesoporous molecular sieves MCM-41 by impregnation of 12-molybdophosphoric acid followed by calcination. The nanochannels of MCM-41 provide a large surface area for the solid state dispersion of 12-molybdophosphoric acid. The samples have been characterized by N-2 adsorption-desorption at -196 degrees C, transmission electron microscopy (TEM), powder X-ray diffraction (PXRD), and FT-IR measurements. The acidity and catalytic activity have been, respectively, examined by nonaqueous titration of n-butylamine in acetonitrile and synthesis of hydroquinone diacetate. The results showed that ordered hexagonal pore structure was observed in the synthesized MCM-41. Also the results indicate that PMA are highly dispersed on mesoporous silica MCM-41 spherical nanoparticles while PMA retains its Keggin structure. On the other hand, with increasing the introduced PMA amount, the specific surface area decreases, and the mesoporous ordering of the samples become poor. Both the surface acidity and the catalytic activity sharply increase with the modification of MCM-41 by PMA but decrease by increasing the calcination temperature. The sample with 55 wt% PMA/MCM-41 calcined at 350 degrees C shows the highest acidity and catalytic activity. (C) 2013 Elsevier B. V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据