A study on nano-sized NiO electrodes doping with C and Co prepared by electrochemical deposition-sintering processes and their capacitance performance

期刊

CHINESE SCIENCE BULLETIN
卷 49, 期 14, 页码 1446-1449

出版社

SCIENCE PRESS
DOI: 10.1360/03wb0190

关键词

super-capacitors; nano-NiO electrode; electrochemical deposition; sintering

向作者/读者索取更多资源

In the present work, it was studied that nano-sized NiO electrodes doping with C and Co were prepared by electrochemical deposition in an ethanol solution containing nickel nitrate and cobalt nitrate and sintering processes. The capacitance performance of such electrodes was also studied. The results reveal that samples obtained by electrochemical deposition first on a porous nickel cathode in an ethanol solution contain 0.5 mol/L nitrates, in which Ni(NO3)(2) and Co(NO3)(2) were mixed in a molar proportion of 8:2. After sintering at 300degreesC for 2 h, they exhibited the best performance. XRD analysis illustrates that the essential phase of the product is NiO doping with certain content of C and Co. The particles of product imaged a spherical morphology with sizes of 20-30 nut in diameter, and with an average crystal size of 4-5 nm. The capacitance measurement of the simulating C/NiO capacitors indicates that a single electrode can reach as high as 410.0 F/g, and still maintain the value of 323 F/g after 30 recycles showed as a stabilized value with increasing recycles, when it was discharged at a current of 5 mA.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.2
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据