Tempered and laser hardened 17-4PH steel; Shot peening; Thermal relaxation; epsilon-Cu precipitate
类别
资金
- Shanghai Electric Power Generation Equipment Co., Ltd. (SEPG) Turbine Works
- Shanghai Carthing Machinery Co. Ltd.
In order to investigate the residual stress relaxations of shot peened layer, isothermal annealing treatments were carried out on tempered and laser hardened 17-4PH steel after shot peening with different temperatures from 300 degrees C to 600 degrees C. The results showed that the residual stresses were relaxed in the whole deformation layer especially under higher temperature. The maximum rates of stress relaxation took place at the initial stage of annealing process in all conditions. The relaxation process during isothermal annealing could be described by Zener-Wert-Avrami function. The thermal stability of residual stress in tempered 17-4PH was higher than that in laser hardened 17-4PH as well as that in alpha-iron, which was due to the pinning effects of epsilon-Cu precipitates on the dislocation movement. As massive epsilon-Cu precipitates formed in the temperature about 480 degrees C, the activation enthalpies for stress relaxation in laser hardened 17-4PH were the same as that in tempered 17-4PH in the conditions of isothermal annealing temperatures of 500 degrees C and 600 degrees C. (C) 2011 Elsevier B. V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据