APPLIED SURFACE SCIENCE
卷 256, 期 2, 页码 513-516出版社
ELSEVIER
DOI: 10.1016/j.apsusc.2009.07.096
关键词
MFM; ZnO; Grain; MOKE
The present study reports the room temperature ferromagnetism in undoped ZnO thin films grown by PVD method. The 500 nm film with small (90 nm) ZnO grains possess isolated magnetic domains with coercivity of 520 Oe. However, long range magnetic ordering with smaller coercivity of 230 Oe is observed for 1000 nm film. The long range ordering is caused by the reduction in domain wall pinning effect due to the presence of bigger (270 nm) ZnO grains. PL measurements show that these grains are semiconducting in nature. Results presented here suggest that oxygen vacancies at the surface may be responsible for the observed ferromagnetism. (C) 2009 Elsevier B. V. All rights reserved.