关键词
plasma; poly(lactide-co-glycolide) (PLGA); cell affinity; shear stress; tissue engineering
In this study, poly (lactide-co-glycolide) (PLGA) films were treated by oxygen plasma. The surface structure. topography and surface chemistry of treated PLGA films were characterized by contact angle measurement, scanning electron microscope observation. atomic force microscopy, and X-ray photoelectron spectrum analysis. The cell affinity of the oxygen plasma treated films was evaluated under dynamic conditions by Parallel Plate Flow Chamber (PPFC). The results showed that the hydrophilicity increased greatly after oxygen plasma treatment. High quantities of -C-O groups, Such as hydroxyl and peroxyl groups could be incorporated into the surface of PLGA (70/30) by controlling appropriate plasma treatment conditions. Moreover, the oxygen plasma treatment resulted in formation of peaks and valleys on the sample surfaces, and the roughness increased with treatment time. Cells stretched very well and the ability to endure the shear stress was improved greatly after the PLGA (70/30) was modified by appropriate plasma treatment. i.e. under 50 W for 2 or 10 min. However, when the treatment time was increased to 20 min, the percentage of adherent cells on the roughest surface decreased because the content of polar groups incorporated onto the surface decreased. The results showed that improved cell adhesion was attributed to the combination of surface chemistry and surface morphology of PLGA during plasma etching. (C) 2003 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据