carbon; nanotubes bundles; alumina membrane; ethylene decomposition; electron microscopy; surface area
Carbon nanotubes were synthesised within the pores of an alumina membrane. The membrane had 200 nm diameter pores and 60 mum thickness, and ethylene was used as carbon source. Membrane dissolution by HF results in a bundle of parallel open tubes, aligned without macroscopic defects. The external diameter of the tubes is uniform and there is no evidence of any amorphous carbon. Wall thickness control was obtained by varying the reaction time, length by the thickness of alumina membrane, and external tube diameter by the membrane pore size. Scanning (SEM) and transmission (TEM) electron microscopy, atomic force microscopy (AFM), X-ray diffraction, thermogravimetric analysis (TG) and surface area evaluation by nitrogen adsorption were used for the characterization of membrane and nanotubes.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据