关键词
bioresorbable; poly-L-lactide; degradation; molecular weight; crystallinity
POLY-L-lactide (PLLA) is one of the most significant members of a group of polymers regarded as bioresorbable. The degradation of PLLA proceeds through hydrolysis of the ester linkage in the polymers's backbone and is influenced by the polymer's initial molecular weight and degree of crystallinity. To evaluate its degradation PLLA pellets were processed by compression moulding into tensile test specimens and by extrusion into 2 mm diameter lengths of rod, prior to being sterilized by ethlene oxide gas (EtO) and degraded in both in vitro and in vivo environments. On retrieval at predetermined time intervals, procedures were used to evaluate the material's molecular weight, crystallinity, mechanical strength, and thermal properties. Additionally, the in vivo host tissue's biological response was analysed. The results from this study suggest that in both the in vitro and in vivo environments, degradation proceeded at the same rate and followed the general sequence of aliphatic polyester degradation, ruling out enzymes contributing and accelerating the degradation rate in vivo. Additionally, the absence of cells marking an inflammatory response suggests that the PLLA rods investigated in vivo were biocompatible throughout the 44 weeks duration of the study, before any mass loss was observed.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据