期刊
JOURNAL OF MATERIALS SCIENCE
卷 39, 期 19, 页码 5987-5994出版社
SPRINGER
DOI: 10.1023/B:JMSC.0000041695.40772.56
关键词
-
LaB(6)-ZrB(2) eutectics were directionally solidified by a zone melting process. The microstructure and crystallography were characterized by X-ray diffraction, optical microscopy and transmission electron microscopy. The anisotropies of hardness and indentation fracture toughness were assessed by making measurements along different crystallographic directions on both transverse and longitudinal sections. While the hardness did not vary appreciably between the two orientations, the fracture toughness was observed to be highly anisotropic. Toughening behavior was observed on longitudinal sections with crack deflection and bridging mechanisms apparent. Cracks were difficult to initiate on transverse sections along directions perpendicular to the growth direction, but for 20 N loads an indentation fracture toughness of 11 MParootm could be measured. (C) 2004 Kluwer Academic Publishers.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据