卷 88, 期 1, 页码 27-31出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.matchemphys.2004.03.023
关键词
ceramics; barium titanate; sintering temperature; dielectric properties
Using powders prepared by a high-gravity reactive precipitation process, grain-controlled barium titanate ceramics were obtained under conventional sintering conditions. X-ray diffraction, scanning electron microscopy, transmission electron microscopy, as well as dielectric measurements were used to characterize the samples. The powder was densified to >95% of theoretical density when sintered at 1200degreesC (K1200), and the average grain size of the resulting ceramics was <0.5 mum. Increasing sintering temperature increased the grain size and did not arise the exaggerated grain growth. The grain size significantly affects the permittivity of the resulting ceramics. Room temperature permittivity of the sample K1200 showed relatively low values (2800) compared with those (typically 4143) for ceramics sintered at 1250degreesC, consisting of larger grains (approximate to1 mum). The lower permittivity was attributed to an incomplete development of the tetragonal structure. (C) 2004 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据