期刊
BULLETIN OF MATERIALS SCIENCE
卷 27, 期 6, 页码 487-489出版社
INDIAN ACADEMY SCIENCES
DOI: 10.1007/BF02707273
关键词
ceramics; oxides; chemical synthesis; X-ray diffraction; microscopy
A gel was formed when a mixture of TiOCl2 and tartaric acid was heated on a water bath. Ultrafine powders of TiO2 in the anatase phase were formed, when the gel was decomposed at 623 K and the mole ratio of tartaric acid to titanium was 2. The anatase phase was converted into rutile phase on annealing at higher temperatures, > 773 K. When initial ratio of titanium to tartaric acid was < 2, the decomposition of gel leads to the formation of mixed phases of rutile and anatase. However, pure rutile phase was not formed by the decomposition of gel for any ratio of tartaric acid and titanium. These powders were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM) and surface area measurements. The average particle size obtained for anatase phase was 3 nm whereas it was 30 nm for rutile phase. Raman scattering experiments were also performed to confirm both anatase and rutile phases.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据