关键词
polypropylene; beta-phase; annealing; UV degradation
Samples of commercial-grade isotactic polypropylene, both neat and nucleated with a specific beta-nucleating agent (N,N-'-dicyclohexylnaphthalene-2,6-dicarboxamide), were exposed to annealing and UV irradiation. Structural parameters were assessed by X-ray diffraction. Tensile mechanical characteristics were derived from stress-strain curves- The specific nucleation caused more than 70% of the crystalline phase to occur in the trigonal beta-modification. The content of the beta-phase introduced by the specific nucleation distinctly decreased after a certain induction period, different for annealing at 140degreesC and UV exposure. At the same time, the size of the alpha-crystallites increased while the size of the beta-crystallites remained virtually unchanged. These results indicate the beta-->alpharecrystallization. On the other hand, the strain-at-break values continuously and monotonically decreased with increasing exposure time reflecting defect formation, both at the surface and in the bulk of the specimens. The differences between the effects of thermal ageing and UV degradation are discussed. (C) 2004 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据