Low-temperature magnetotransport behaviors of heavily Mn-doped (Ga,Mn)As films with high ferromagnetic transition temperature

We report the low-temperature magnetotransport behaviors of (Ga,Mn)As films with the nominal Mn concentration x larger than 10%. The ferromagnetic transition temperature T-C can be enhanced to 191 K after postgrowth annealing (Ga,Mn)As with x=20%. The temperature T-m, corresponding to the resistivity minimum in the curve of resistivity versus temperature at temperature below T-C, depends on Mn concentration, annealing condition, and magnetic field. Moreover, we find that the variable-range hopping may be the main conductive mechanism when temperature is lower than T-m.