期刊
THERMOCHIMICA ACTA
卷 425, 期 1-2, 页码 75-89出版社
ELSEVIER
DOI: 10.1016/j.tca.2004.06.009
关键词
boehmite; transition alumina; non-isothermal kinetics; computer simulation
First, the structural features of nanocrystalline boehmite synthesized by hydrolysis of aluminum sec-butoxide according to the Yoldas method are reported. The nanosized boehmite consists of rectangular platelets averaging 8 by 9 nm and 2-3 nm in thickness which contain a large excess of water. Dehydration by heating under vacuum induced an increase in the specific surface area, down to a minimum water content (similar to0.2 H2O per Al2O3); values up to 470 m(2)/g can be reached. However this enlargement of specific surface area only results from water loss, the surface area remaining constant. The particle morphology, the excess of water, as well as the specific surface area, depend on the amount of acid used for the peptization during the synthesis. Second, a comprehensive investigation of the dehydration kinetics is presented. The simulations of the non-isothermal experiments at constant heating rates show that thermally stimulated transformation of nanocrystalline boehmite into alumina can be accurately modeled by a 4-reaction mechanism involving: (I) the loss of physisorbed water, (II) the loss of chermsorbed water, (III) the conversion of boehmite into transition alumina, (IV) the dehydration of transition alumina (loss of residual hydroxyl groups). The activation energy of each step is found to be very similar for experiments done in various conditions (heating rate, atmosphere, kind of sample,...). (C) 2004 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据