FePt; granular-type structure; magnetic anisotropy; perpendicular; magnetic recording media; spin stand
Perpendicular magnetic recording media, composed of granular-type FePt-MgO films on Fe-Ta-C soft magnetic underlayer (SUL), have been fabricated on to 2.5-in glass disks. (001) textured FePt granular films with high-perpendicular magnetic anisotropy were obtained by annealing the FePt/MgO multilayer films. The FePt grain size, perpendicular coercivity, magnetic activation volume, and the exchange coupling between the FePt grains were found to be strongly dependent on the initial multilayer structures and the annealing conditions. The recording performance of the disks was evaluated by a spin-stand. The obtained results reveal a close correlation between the recording performance and magnetic properties. The thermal stability of the granular-type FePt media was studied using high-temperature magnetic force microscopy (MFM) technique, equipped with in situ sample heating, in the temperature range 25degreesC-200degreesC. The estimated signal decay at high temperature is ascribed to the temperature dependent magnetic anisotropy behavior.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据