期刊
SOLID STATE IONICS
卷 176, 期 5-6, 页码 621-627出版社
ELSEVIER
DOI: 10.1016/j.ssi.2004.09.004
关键词
sonochemistry; manganese oxide; acetylene black; nanocomposite
Nanostructure and high-rate discharge-charge capacities were investigated for the manganese oxide/acetylene black (AB) nanocomposites fabricated by sonication from aqueous solutions containing permanganate ion. Coating structure in which the acetylene black particles were uniformly coated with manganese oxide was successfully prepared from a pH=10 solution. On the other hand, acicular and tabular birnessite crystals were observed in samples obtained from pH<1 solutions, although the formation rate of manganese oxide in the pH<1 solution was much faster than that in the pH=10 solution. The sample from the pH=10 solution could be discharged and charged under high current density, such as 10 A g(-1), because of the unique nanostructure. In contrast, a large decrease in the specific capacity was observed for the sample synthesized from the pH<1 solution under 10 A g(-1) due to the excessive formation of manganese oxide and the disadvantage in the electronic conduction and lithium diffusion of the birnessite. (C) 2004 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据