APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING
卷 98, 期 1, 页码 211-217出版社
SPRINGER HEIDELBERG
DOI: 10.1007/s00339-009-5375-z
关键词
-
资金
- Natural Science Foundation of Tianjin City [07JCZDJC01200]
- National Natural Science Foundation of China
- Shanghai Baosteel Group Company [50834011]
The three cooling rates of 10, 100, 200 K/min dilatometry experiments are used to investigate the kinetics of the isochronal austenite (gamma) to ferrite (alpha) transformation of Fe-0.0036wt.%C alloy. Normal transformation and abnormal transformation have both been observed for transformations at different cooling rates. In accordance with the thermodynamic characteristics of the gamma ->alpha transformation investigated here and previous kinetic considerations, a JMAK-like approach for the kinetics of isochronal phase transformations was developed that incorporates three overlapping processes: site saturation nucleation, alternate growth modes (from interface-controlled to diffusion-controlled to interface-controlled growth), as well as impingement for random distribution nuclei. The JMAK-like approach has been employed to fit the experimental results, and the fitting results show that for the gamma ->alpha transformation of the Fe-C alloy at all applied cooling rates, the growth mode evolves in the corresponding order: from interface-controlled to diffusion-controlled growth; from interface-controlled to diffusion-controlled to interface-controlled growth; and interface-controlled growth.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据