Effect of boron concentration Y2O3:(Eu,B) phosphor on luminescence property

Y2O3:(Eu,B) red phosphor was obtained by a thermal decomposition technique of a mixture of yttrium-ethylenediaminetetraacetic acid (Y-EDTA), Eu-EDTA and boric acid. The doping ratio of boron, [B]/([Y] + [Eu]), in the starting material was varied from 0 to 1. The properties of morphology, crystallization behavior, metal composition and photoluminescence of resulting Y2O3:(Eu,B) powder were examined. The Y2O3:(Eu,B) powder had spherical shape with a diameter of 1-5 mu m with some hollows on the surface. No secondary cohesive particles were seen. X-ray diffractometry revealed that although the crystallinity of powder was improved with addition of small amounts of boron, it decreased with excess amounts of boron. Several peaks indexed as the impurity phases of Y3BO6 and YBO3 were observed on the samples obtained under condition of excess amounts of boron. The photoluminescence intensity observed at 611 nm was dependent upon crystallinity of the sample. (c) 2005 Elsevier Ltd. All rights reserved.