Changes in electronic structure upon lithium insertion into the A-site deficient perovskite type oxides (Li,La)TiO3

Investigation on variation of the electronic structure accompanying the electrochemical lithium insertion into the perovskite type oxide, (Li,La)TiO3, has been carried out by X-ray absorption spectroscopy (XAS). During the electrochemical lithium insertion, titanium ion reduced its oxidation state from Ti4+ to Ti3+, while La3+ does not contribute to the reduction reaction resulting from Ti K-edge and La L-3-edge XAS, respectively. Furthermore, O K-edge XAS showed marked spectral changes with electrochemical lithium insertion, indicating the electronic structure around oxide ion affected by lithium insertion reaction. From the XAS measurement, we have concluded the variation observed in O K-edge XAS was related to the strong interaction with inserted Li ion. To confirm this, first-principles band calculations were performed for the perovskite structure before and after electrochemical lithium insertion. The calculated results showed that the electron originated from inserted Li transferred to neighboring oxide ion locally as well as to Ti ion. This may be due to local neutralization effect of Li to reduce the electrostatic interaction in the crystal.