卷 142, 期 1-2, 页码 292-297出版社
ELSEVIER
DOI: 10.1016/j.jpowsour.2004.10.015
关键词
lithium-ion batteries; nanocrystalline thin film; transition metal ferrite MFe2O4 (M = Cu, Ni, Co)
Nanocrystalline ferrite MFe2O4 (M=Cu, Ni, Co) thin films have been prepared by an electrochemical route involving cathodic electrodeposition of MFe2 alloys and further anodization of the alloy films at room temperature. XRD measurements showed that those films are polycrystalline with spinet tetragonal structure for CuFe2O4, and cubic structure for NiFe2O4 and CoFe2O4, respectively. The uniform MFe2O4 films without cracks and pinholes were observed in SEM measurement, and the estimated grain average sizes of as-prepared ferrite films were about 50nm. The electrochemical measurements showed that MFe2O4 thin film electrodes delivered a reversible capacity of 450-460mAhg(-1) at 10 mu Acm(-2) in the voltage range of 0.01-3.0V and more than 75% reversible capacity still remained up to 100 cycles. Our results showed that MFe2O4 thin films could be used as promising anode materials for thin film lithium-ion batteries. (c) 2004 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据