MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY
卷 117, 期 3, 页码 231-234出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.mseb.2004.11.028
关键词
sintering behaviors; Bi2O3-WO3 additives; initial permeability; Q-factor
The effects of mixed Bi2O3-WO3 additives on sintering behaviors and magnetic properties of NiCuZn ferrites were investigated. It was confirmed that appropriate additives of mixed Bi2O3-WO3 could enhance densification of specimens, improve initial permeability and Q-factor of NiCuZn ferrites. This was mainly attributed by that appropriate WO3 additive could improve grain size of the specimen and closed pores are not formed. The maximum initial permeability was achieved with 1.5 wt% Bi2O3 and 0.3 wt% WO3 additives. More WO3 additive may result in the abnormal grain growth and closed pores inside the grain. The multilayer chip inductor made by composition with 1.5 wt% Bi2O3 and 0.3 wt% WO3 additives exhibited relatively lower dc resistivity, higher inductance and Q-factor than the inductor made by NiCuZn ferrite with only Bi2O3 added, this was mainly due to relatively less diffusion of Ag internal electrode and higher initial permeability. (c) 2004 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据