期刊
ACTA MATERIALIA
卷 53, 期 7, 页码 2081-2089出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.actamat.2005.01.020
关键词
nanostructured; low carbon steel; surface mechanical attrition treatment; high store energy; chromizing; diffusion
A nanostructured surface layer of about 20 mu m thick was produced in a low carbon steel plate by means of the surface mechanical attrition treatment (SMAT). Chromizing behaviors of the SMAT sample were investigated by using X-ray diffraction, scanning electron microscopy and transmission electron microscopy. Experimental results showed that a much thicker Cr-diffusion layer was obtained in the SMAT sample than in the coarse-grained one after the same chromizing treatment, especially at low temperatures. In the SMAT sample, the formation temperature of chromium compounds was found to be much lower and the amount of chromium carbides was higher than those in the coarse-grained counterpart. The enhanced chromizing kinetics originates from numerous grain boundaries with a high excess stored energy in the nanostructured surface layer due to severe plastic deformation during the SMAT. (c) 2005 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据