期刊
JOURNAL OF MOLECULAR STRUCTURE
卷 739, 期 1-3, 页码 153-161出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.molstruc.2004.04.034
关键词
proton; conductivity; polyelectrolyte; fuel cell; phosphoric acid
New proton-conducting polymer electrolyte membranes having phosphoric acid groups have been systematically synthesized. These homopolymers and copolymers were prepared by a conventional radical polymerization and a copolymerization with acrylonitrile or styrene or similar materials. The phosphoric acid groups can be cross-linked by heat treatments at 100 degrees C, and hence their membranes showed excellent mechanical properties and chemical stability. Measurements of the water absorption and differential scanning calorimetry revealed that the copolymer membranes absorbed smaller amounts of water, which is freezing water under 90% RH, compared with the sulfonated polyelectrolyte membranes. The proton conductivity of the P-PHM membranes hydrated was measured to be 5.0 x 10(-3) S cm(-1) at 100 degrees C. This value was usually maintained up to 160 degrees C. Dried homopolymer membranes and copolymer membranes were also examined for the water absorption and proton conductivity. It was found that the copolymerization with acrylonitrile provided good film-forming properties, thermal stability, and useful control of the physical and electrochemical properties. (c) 2004 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据