In this letter, we investigate the impact of rapid thermal annealing (RTA) on thin-film polycrystalline silicon (pc-Si) solar cells on glass made by evaporation of amorphous silicon (a-Si) and subsequent solid-phase crystallization (SPC). These devices have the potential to deliver low-cost photovoltaic electricity and are named EVA cells (SPC of EVAporated a-Si). The RTA is used to perform a high-temperature (> 700 degrees C) process for point defect annealing and dopant activation. RTA processes have predominantly been developed for wafer-based devices yet also have great potential for low-temperature devices such as thin-film pc-Si on glass solar cells. Parameter variations are performed on EVA solar cells to determine optimum values for point defect removal and dopant activation while minimizing dopant diffusion causing junction smearing. The I-Sun open-circuit voltage, V-oc, of the as-crystallized pc-Si devices is rather modest (135 mV). However, after RTA and subsequent hydrogen passivation in a rf PECVD plasma, a V-oc of 454 mV is realized, representing a large improvement by a factor of 3.4. With an optimized passivation and dopant profile, a V-oc greater than 500 mV is well within the reach of the EVA technology. (c) 2005 American Institute of Physics.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据