Etching technique for revelation of plastic deformation zone in low carbon steel

In this study, an etching technique to detect the localised plastic deformation behaviour in a low carbon steel was developed. With this technique, etching with Fry solution under ultrasonic vibration was carried out on samples plastically deformed and then heated at 550 degrees C for a certain period of time. The plastic zone was revealed by different degrees of etching in the plastically deformed and non-deformed regions; the plastic zone was found to be only slightly etched, whereas the other region was deeply etched. From the surface offset after etching, the deformation zone was found to be observable even at low magnification, such as 10 times. As the heating duration increased, the plastic zone became clearer. The mechanism for such an etching reaction is discussed on the basis of electrochemical analysis.