卷 26, 期 15, 页码 2415-2422出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.biomaterials.2004.07.067
关键词
polylactic acid; degradation; mechanical properties; x-ray diffraction (XRD); microstructure
Addition of lauric acid to Poly (L-lactide) (PLLA) has resulted in a new family of enhanced degradation biomaterials. Presented is PLLA4.5 (PLLA containing 4.5 wt% lauric acid), the fastest degrading of the family. Degradation was studied via mass changes, gel-permeation chromatography, wide- and small-angle X-ray scattering (WAXS and SAXS), simultaneous SAXS and tensile testing, and visual observation. The undegraded PLLA4.5 deformed by crazing, recognisable from the characteristic shape of the SAXS pattern. As water up-take and degradation proceeded,samples crystallised, decreasing the SAXS long period, until by 4 days the deformation mechanism had become that of crystal-mediated deformation. This resulted in a 'peanut lemon'-shaped SAXS pattern, interpreted in terms of cavitation and fibrillated shear. Further degradation up to 12 days resulted in the same deformation mechanism at different sample displacements, with samples failing earlier during tensile testing until a ductile-brittle transition occurred. At 30-40 days water up-take and mass-loss increased significantly and global whitening of samples occurred, while the crystallinity and long period stabilised. Complete degradation had not occurred by the end of the study at 73 days. Through an understanding of how the changes in morphology during degradation affect the micromechanisms of deformation, it may be possible to design microstructures to give a tailored evolution of mechanical response in the body. (C) 2004 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据