The properties and the applicability of iron- and cobalt-containing perovskites were evaluated as cathodes for solid oxide fuel cells (SOFCs) in comparison to state-of-the-art manganite-based perovskites. The materials examined were Laj(1-x-y)SrCo(0.2)Fe(0.8)O(3-delta) (x = 0.2 and 0.4; y = 0-0.05), La0.8Sr0.2FeO3-delta, La0.7Ba0.3Co0.2Fe0.8O3-delta and Ce0.05Sr0.95Co0.2FeO0.8O3-delta. The main emphasis was placed on the electrochemical properties of the materials, which were investigated on planar anode-supported SOFCs with 8 mol% yttria-stabilised zirconia (8YSZ) electrolytes. An interlayer of the composition Ce0.8Gd0.2O2-delta was placed between the electrolyte and the cathode to prevent undesired chemical reactions between the materials. The sintering temperatures of the cathodes were adapted for each of the materials to obtain similar micro structures. In comparison to the SOFCs with state-of-the-art manganite-based cathodes, SOFCs with La1-x-ySrCo0.2Fe0.8O3-delta cathodes achieved much higher current densities. Small A-site deficiency and high strontium content had a particularly positive effect on cell performance. The measured current densities of cells with these cathodes were as high as 1.76 A/cm(2) at 800 degrees C and 0.7 V, which is about twice the current density of cells with LSM/YSZ cathodes. SOFCs with La0.58Sr0.4Co0.2Fe0.8O3-delta cathodes have been operated for more than 5000 h in endurance tests with a degradation of 1.0-1.5% per 1000 h. (c) 2005 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据