JOURNAL OF APPLIED POLYMER SCIENCE
卷 96, 期 4, 页码 983-991出版社
WILEY
DOI: 10.1002/app.21002
关键词
conducting polymers; fibers; nylon
For the preparation of conducting polyaniline (PANI)/nylon composites with high electrical conductivity as well as superior mechanical properties such as flexibility and lightness, PANI/nylon-6 composite nanofiber webs were prepared via the electrospinning process with a nylon-6/formic acid polymer solution, and then PANI on the surface of the nylon-6 electrospun nanofiber webs was chemically polymerized. The electrical conductivity measurements showed that the conductivity of the PANI/nylon-6 composite electrospun fiber webs was superior to that of PANI/nylon-6 plain-weave fabrics because of the high surface-area/volume ratios. On the other hand, the volume conductivities of the PANI/nylon-6 composite electrospun fiber webs increased from 0.5 to 1.5 S/cm as the diffusion time increased from 10 min to 4 h because of the even distribution of PANI in the electrospun fiber webs. However, the surface conductivities of the PANI/nylon-6 composite electrospun fiber webs somewhat decreased from 0.22 to 0.14 S/cm as the diffusion time increased because of PANI contaminated with aniline monomers, aniline oligomers, and some alkyl chains, which served as electrical resistants. These results were confirmed with Fourier transform infrared, electron spectroscopy for chemical analysis, and morphology analysis. It was concluded that the diffusion time for the in situ polymerization of PANI in electrospun fiber webs was optimized at approximately 3 h. (c) 2005 Wiley Periodicals, Inc.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据