关键词
MOVPE; CuGaS2; Cu(hfac)(2); NEt3
Epitaxial growth of CuGaS2 using atmospheric pressure metalorganic (MO) vapour phase epitaxy (MOVPE) was carried out using two different copper metalorganic precursors, namely, cyclopentadienyl copper triethylphosphine (CpCuTEP) and hexafluoroacetylacetate copper triethylamine (Cu(hfac)(2) (.) NEt3). A change in the Cu content (most significant for epilayers grown using the former precursor) was found to occur along the flow direction. A study using X-ray diffiractometry could not conclusively determine which of the possible structure types were present in the epilayer. Analysis of the transmission electron diffraction (TED) patterns using the < 211 > zone axes indicates that a mixture of disordered zinc blende and CuPt-type ordering occurs in both types of epilayers, whereas a tetragonal crystal structure (chalcopyrite or CuAu-type ordering) likely occurs within surface crystallites found in epilayers grown using Cu(hfaC)2 (.) NEt3. The photoluminescence (PL) for both epilayers consisted of a broad band at 580-620 nm, typical of Ga-rich material. (c) 2004 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据