期刊
APPLIED ENERGY
卷 112, 期 -, 页码 1357-1366出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.apenergy.2013.04.050
关键词
Metal foam; Composite phase change materials; Thermal characterization
The utilization of paraffin in the latent thermal energy storage (LTES) system for solar energy storage is hampered by its low thermal conductivity. Paraffin/nickel foam and paraffin/copper foam composite phase change materials (PCMs) were prepared using a vacuum impregnation method in the present study. The impregnation ratios which reflect the actual mass fraction of pure paraffin impregnated were studied comparatively for the impregnations with and without vacuum assistance. The surface porosity was obtained by employing the image processing approach. The thermal conductivities of the composite PCMs were measured by the transient plane heat source technique (TPS) as well as the steady state method, and the thermal behaviors were analyzed with a differential scanning calorimeter (DSC). It is found that the surface porosity obtained from image analysis was in the range of 90-94%, whereas the bulk porosity predicted by the mass fraction was about 97%. Compared with pure paraffin, the thermal conductivities of the composite PCMs were drastically enhanced, e.g., the thermal conductivity of the paraffin/nickel foam composite was nearly three times larger than that of pure paraffin. The presence of porous metal foam made the phase change temperatures shift slightly, e.g., the deviations of the peak melting temperatures of the paraffin/nickel foam composite and paraffin/copper foam composite with the pore size of 25PPI from those of pure paraffin were 0.55 degrees C and 0.40 degrees C, respectively. (C) 2013 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据