期刊
APPLIED CLAY SCIENCE
卷 53, 期 4, 页码 676-683出版社
ELSEVIER
DOI: 10.1016/j.clay.2011.06.003
关键词
Mesoporous; Pillared-clay; Intercalate; Montmorillonite; Aluminosilicates; Aluminum
资金
- Social Development Program of Jiangsu Province [BE2009637]
Mesostructured aluminosilicate intercalates have been prepared by the post synthesis grafting of aluminum onto the mesostructured interlayer space silica framework of a silica-pillared clay (SPC) precursor derived from the natural montmorillonite. Elemental analyses, powder X-ray diffraction (XRD), scanning electron microscopy (SEM), N-2 adsorption-desorption isotherms, and Al-27 MAS NMR spectroscopy were used to characterize the products, which we designate Al-SPC. The Al-SPC derivatives exhibited basal spacings of 3.2-3.4 nm, BET surface areas of 444.8-806.7 m(2)/g, and pore sizes in the large micropore to small mesopore range (1.5-1.6 nm). The aluminum content was strongly correlated with the Si/Al stoichiometry of the post synthesis reaction mixture. Nearly all of the grafted aluminum was incorporated into tetrahedral sites in the interlayer silica framework. The alumination reagents afforded protonated Al-SPC derivatives with increased acidity in comparison to the initial silica-intercalated SPC precursor, as catalytic reactivity for cumene cracking. (C) 2011 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据