Depth profiles of electronic structure at the interface between Cu(In1-xGax)Se-2 (CIGSe) grown by three-stage process and US through chemical bath deposition have been studied by ultraviolet X-ray photoelectron spectroscopy (UPS, XPS) and inverse photoemission spectroscopy (IPES). Especially, a dependence of band alignment on Ga content in the CIGSe was investigated. An intrinsic feature at an arbitrary depth was successfully exposed by etching with an Ar ion beam with a low ion energy of 330 eV After the removal of surface contamination, the US layer exhibited a band gap of 2.4 eV The band gap started to shrink when XPS core signals of CIGSe became detectable. For the interface over the CIGSe with a Ga substitution ratio x of 0.20%, valence band offset (VBO) was about 0.7 eV, and conduction band offset (CBO) looked finite. An increase of the Ga substitution ratio to 0.40 resulted in an increase of the VBO and a reduction of the CBO. An almost flat conduction band alignment was observed at the interface of CdS/Cu-0.93(In0.60Ga0.40)Se-2. (c) 2004 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据