卷 46, 期 14, 页码 5133-5139出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.polymer.2005.04.039
关键词
nanofibers; poly(acrylic acid); electrospinning
Ultra-fine polyelectrolyte fibers have been generated front electrospinning of poly(acrylic acid) in aqueous and DMF solutions. The fiber diameters ranged from 80 to 500 nm and increased with increasing solution concentrations and electrospinning voltages. The fibers generated from the aqueous solutions were more homogeneous in sizes, especially when NaCl or NaOH was added. Higher voltages in electrospinning of the aqueous solutions also resulted in fibers with larger heat capacity in the glass transition region, and higher dehydration temperatures. These polyelectrolyte fibers could be rendered water-insoluble by incorporating beta-cyclodextrin (at 20 wt% of PAA) in the aqueous solution, then heat-induced crosslinking was performed at 140 degrees C for 20 min. The resulting hydrogel fibers showed strongly pH-responsive swelling behaviors. (c) 2005 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据