OXIDATION OF METALS
卷 64, 期 1-2, 页码 23-41出版社
SPRINGER/PLENUM PUBLISHERS
DOI: 10.1007/s11085-005-5704-3
关键词
oxidation; KCl; deposit; breakaway corrosion; 304L; chromate
The influence of KCl on the oxidation of the 304-type (Fe18Cr10Ni) austenitic stainless steel at 600 degrees C in 5% O-2 and in 5% O-2 + 40%H2O is investigated in the laboratory. The samples are coated with 0.1 mg/cm(2) KCl prior to exposure. Exposure time is 1-168 h. Uncoated samples are exposed for reference. The oxidized samples are analyzed by ESEM/EDX, XRD and AES. The results show that small additions of potassium chloride strongly accelerate high temperature corrosion, the oxide thickness being up to two orders of magnitude greater after exposure in the presence of KCl. The rapid corrosion is initiated by the formation of potassium chromate through the reaction of KCl with the protective oxide. Chromate formation is a sink for chromium in the oxide and leads to a loss of its protective properties. The resulting rapidly growing scale consists of an outer hematite layer with embedded K2CrO4 particles and an inner layer consisting of spinel oxide, (Fe,Cr,Ni)(3)O-4. Little or no chlorine is found in the scale or at the scale/metal interface.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据