PROCEEDINGS OF THE IEEE
卷 93, 期 8, 页码 1451-1458出版社
IEEE-INST ELECTRICAL ELECTRONICS ENGINEERS INC
DOI: 10.1109/JPROC.2005.851515
关键词
flexible displays; flexible substrates; indium tin oxide (ITO)
As opto-electronic devices become flexible, the designing of reliable devices becomes more challenging. In this paper, we focus on the degradation of flexible transparent anodes by mechanical and thermal stresses. Indium tin oxide (ITO)-coated polyethyleneterephthalate (PET) is susceptible to cracking at low strains (< 2%), but has excellent electrical and optical characteristics. Conducting polymers, such as polyethylene dioxythiophene doped with polystyrene sulfonate (PEDOT:PSS), have good mechanical properties, but are severely degraded by temperature, and have inferior optical and electronic properties. We have developed a mandrel-bending automated test system to evaluate the degradation of flexible anodes in service, and find that even when the strain is below the virgin cracking threshold, there are measurable changes in ITO resistance. Cyclic loading of ITO-coated PET shows three regimes of resistance increase: 1) an increase in resistance, due to changes in sample dimension until equilibrium width is obtained (50-100 cycles); 2) a gradual linear increase in resistance, possibly due to cracking of ITO; and 3) a catastrophic failure after 50 000 cycles clue to severe cracking. For PEDOT PSS-coated PET the resistance does not increase significantly with increasing tensile strain, and it is also less susceptible to damage from repeated bending.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据