JOURNAL OF POWER SOURCES
卷 146, 期 1-2, 页码 319-322出版社
ELSEVIER
DOI: 10.1016/j.jpowsour.2005.03.130
关键词
lithium battery; Fe3O4; nanoparticle; high capacity
The lithium battery using Fe3O4 fine particles has been constructed. The discharge characteristics were improved by the addition of India ink or polyvinyl alcohol (PVA). The discharge potential at 60 degrees C maintained 2.5 V versus Li/Li+ up to 500 mAh g(-1) and was 1.8 V at a large capacity of 926 mAh g(-1). The possibility of secondary battery was discussed from the result of cycling test with 926 mAh g(-1). Similar potential curve was obtained in the second cycle. Although degradation was observed in the third cycle, cyclability was maintained. However, the test cell stopped in fourth discharge. It is concluded that a, large capacity was achieved at 60 degrees C using fine particles of Fe3O4 with PVA additive. According to the cycling test, it is expected to be a secondary battery by further development in nanostructure of the cathode. (c) 2005 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据