JOURNAL OF POWER SOURCES
卷 147, 期 1-2, 页码 227-233出版社
ELSEVIER
DOI: 10.1016/j.jpowsour.2004.12.041
关键词
lithium secondary battery; silicon powder anode; copper electroless deposition; annealing; galvanostatic intermittent titration; cycle performance
in order to enhance the electrical conductivity of Si powder, which shows a poor cycleabilty as the anode in lithium secondary batteries due to low electrical conductivity and a severe volume change on cycling, Cu is deposited on the Si surface by a electroless deposition method. As Cu deposition on bare Si powder is found to be unsatisfactory, Si powder is etched to roughen the surface, on to which a large amount of Cu deposit with a uniform coverage is obtained. The resulting anode material exhibits improved cycle performance as a result of conductivity enhancement. The long-term cycleability is, however, still unsatisfactory due to detachment of Cu from the Si surface that is caused by a severe volume change of the Si particles on cycling. The detachment of Cu is greatly suppressed by annealing at 400 degrees C in an inert atmosphere and, thereby, delivers better cycle performance. The improvement in interfacial stability exhibited by the annealed samples is ascribed to the formation of a Cu3Si alloy phase at the interface and diffusion of Cu atoms into the Si particles. (c) 2005 Elsevier B.V. All fights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据