Chromate reduction in wastewater at different pH levels using thin iron wires - A laboratory study

The effectiveness of using thin zero-valent iron (Fe 0) wires in the treatment of wastewater generated from a metal cleaning facility and with a pH in the range of 2 to 10 was examined. It was found that (1) when the sample containing low levels of total chromium <= 14 mg/L was mixed with iron wires at a pH of 3 to 8, 50 to 90% of the total chromium could be reduced in 4 h; (2) the initial reduction efficiency was pH-dependent: the lower the pH, the higher the reduction rate; (3) variations of solution pH, redox electrical potential, and electrical conductivity (EC) in samples were also pH-dependent; (4) the adsorption/reduction efficiency was limited by the diffusion of Cr(VI) from wastewater to the iron surface when the test duration was long; (5) when the initial pH = 3, iron corrosion and redox reaction dominated the reduction process; however, with pH = 8 or 10, corrosion, surface passivation, or metal precipitation could compete with reduction; (6) the used iron wires were still effective in chromium removal in new samples at pH = 3; and (7) some desorption of adsorbed chromium was observed in acidic samples when the test duration was long. Scanning electron microscope images and energy-dispersive X-ray spectra collected from iron samples also indicate that the efficiency of chromium adsorption/reduction is pH-dependent. Our results suggest that using zero-valent iron to polish acidic wastewater containing low contents of chromium and other heavy metals is feasible.