期刊
JOURNAL OF POWER SOURCES
卷 150, 期 -, 页码 120-128出版社
ELSEVIER
DOI: 10.1016/j.jpowsour.2005.03.180
关键词
sulfonated poly(ether ether ketone) (SPEEK); water vapor uptake; proton conductivity; fuel cell performance; temperature; relative humidity
Sulfonated poly(ether ether ketone)s (SPEEKs) with various sulfonation degrees were prepared and characterized for the intention of fuel cell applications. Two distinct water vapor activity regions characterized by different water vapor uptake behaviors were observed. Proton conductivity of SPEEK membranes increases with increasing sulfonation degrees and temperatures. SPEEK membranes with sulfonation degrees of 5 1 and 60% show proton conductivity higher than 0.01 S cm(-1) at temperatures higher than 40 degrees C with 100% relative humidity (RH). Relative humidity has a stronger effect on the proton conductivity of SPEEK membranes than that of Nafion (R) membranes. Fuel cell performance with SPEEK membranes was studied at various temperatures and relative humidities. Good fuel cell performance was obtained with a SPEEK-51 membrane at 80 degrees C, 100% relative humidity and ambient pressure. Both temperature and relative humidity have important influence to the cell resistances and performances. Cyclic voltammetry (CV) as well as hydrogen crossover profiles show distinct features under different relative humidity conditions. (c) 2005 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据