期刊
JOURNAL OF PHYSICAL CHEMISTRY B
卷 109, 期 40, 页码 18772-18776出版社
AMER CHEMICAL SOC
DOI: 10.1021/jp051294j
关键词
-
A simple one-step hydrothermal method for large-scale synthesis of ultralong single-crystalline Bi2S3 nanowires was reported, and the nanowires were comprehensively characterized. The diameters of the nanowires are about 60 nm, and their lengths range from tens of microns to several millimeters. The structure of the nanowires was determined to be of the orthorhombic phase, the growth direction was along [001], and the growth mechanism was investigated based on extensive high-resolution transmission electron microscopy observations. Optical absorption experiments revealed that the Bi2S3 nanowires are narrow-band semiconductors with a band gap E-g approximate to 1.33 eV. Electrical transport measurements on individual nanowires gave a resistivity of about 1.2 Omega cm and an emission current of 3.5 mu A at a bias field of 35 V/mu m. This current corresponds to a current density of about 10(5) A/cm(2), which makes the Bi2S3 nanowire a potential candidate for applications in field-emission electronic devices.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据