MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
卷 407, 期 1-2, 页码 322-329出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2005.07.042
关键词
Al-Si-Mg alloy; Chevron marks; defects; elongation; fracture; shrinkage porosity
A study of the tensile behaviour of test coupons that were extracted from cast plates of D357 aluminium is described. The effects of specimen thickness, heat treatment, structural integrity and hot isostatic pressing (HIP) were investigated. Chevron marks were found on the fracture surfaces of the specimens that failed under plane strain conditions. In most cases, structural defects, such as shrinkage pores and oxide films, were found at the initiation sites for fracture. It is shown that the structural defects that were found at the origin of the chevron patterns are large enough to explain the fractures, and that the tensile failure of cast Al-7Si-Mg alloys can be explained in terms of the principles of fracture mechanics. The influence of structural defects on the elongation to fracture is discussed, together with some implications for quality control programs involving cast Al-7Si-Mg components. (c) 2005 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据