期刊
MATERIALS LETTERS
卷 59, 期 27, 页码 3427-3430出版社
ELSEVIER
DOI: 10.1016/j.matlet.2005.06.008
关键词
nanosized; synthesis; ZSM-5 zeolite; X-ray techniques; mechanism
Nanosized ZSM-5 zeolite was successively synthesized in the absence of organic template by hydrothermal method. About 15 nm ZSM-5 zeolite was synthesized at 180 degrees C for 24 h after stirring at high speed and aging in the synthesis mixture with the molar composition of 12Na(2)O: 100SiO(2):2Al(2)O(3):2500 H2O. X-ray diffraction (XRD) confirmed ZSM-5 crystal phase. Transmission electron microscopy (TEM) showed that ZSM-5 zeolite crystal sizes are about 15 nm. The electron diffraction spectroscopy (EDS) shows nanosized ZSM-5 zeolites chemical element compound. Fourier transform infrared (FTIR) analysis further showed that they are pentacyclic with typical absorption summit of ZSM-5 at about 550 cm(-1). Differential thermal analysis and thermogravimetry analysis (DTA/TG) showed that, at room temperature to 1073 K, nanosized ZSM-5 mass loss is 5.836%. (C) 2005 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据