JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART A
卷 75A, 期 2, 页码 365-373出版社
WILEY
DOI: 10.1002/jbm.a.30430
关键词
calcium phosphate deposition; CoCr alloys; implant failure
Physical wear of orthopedic implants is inevitable. CoCr metal samples, typically used in joint reconstruction, corrode rapidly after removal of the protective oxide layer. The behavior of CoCr pellets immersed in human serum, fetal bovine serum (FBS), synovial fluid, and water were studied using time-of-flight secondary ion mass spectroscopy (ToF-SIMS). The differences in the corrosive nature of human serum, FBS, synovial fluid, and water after 5 days immersion were highlighted by the oxide/hydroxide layer, which was, respectively, 25, 10, 1.5, and 3-3.5 mu thick. The thickness of calcium phosphate deposit from human serum, FBS, and synovial fluid was, respectively, 30, 20, and 2 nm. Co and Cr ions migrated from the bulk metal surface and were trapped in the serum deposits, where chromium existed as oxides, hydroxides, and phosphates, whereas the cobalt chemistry was dominated only by phosphates and hydroxides. This may account for the composition of wear debris from CoCr orthopedic implants, which are predominantly hydroxyphosphate compounds. From the literature, proteoglycans, pyrophosphates, phospholipids, lubricin, and superficial zone protein (SZP) have been identified as possible causes for the insignificant deposit of calcium phosphate from synovial fluid. Circulation of these compounds around the whole implant may inhibit calcium phosphate deposition and therefore contribute to osteolysis. (c) 2005 Wiley Periodicals, Inc.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据