Room temperature photoluminescence at 1.6 mu m is demonstrated from InGaAs quantum dots capped with an 8 nm GaAsSb quantum well. Results obtained from various sample structures are compared, including samples capped with GaAs. The observed redshift in GaAsSb capped samples is attributed to a type II band alignment and to a beneficial modification of growth kinetics during capping due to the presence of Sb. The sample structure is discussed on the basis of transmission electron microscopy results. (C) 2005 American Institute of Physics.