期刊
POLYMER
卷 46, 期 25, 页码 11213-11218出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.polymer.2005.10.044
关键词
cationic polymerization; emulsion; poly(methylhydrogenosiloxane)
The preparation of 2,4,6,8-tetramethylcyclotetrasiloxine (D-4(H)) miniemulsions stabilized by commercial surfactants, i.e. sodium 4 dodecylbenzencsulfonate (NaDBSA) and sodium laurate/lauric acid mixture, Was Studied and is first reported. Then, the pH Was tuned in order to process polymerization through interfacial protonic initiation. With lauric acid, no polyinerization was observed, even at high temperature or large acid contents. Such effect is ascribed to the poor dissociation and reactivity of high pKa's carboxylic acids. With NaDBSA, acidification by HCl was enough to initiate the polymerization, but the pH of the continuous phase was shown to have a strong effect on the polymerization process. Optimal conditions (at pH 5) gave ChaillS With average number molar masses around 16,000 g mol(-1) and polydispersity index close to 1.6, for a total conversion in polymer of about 60% after 2 h reaction. Lower pH (4.2) quickly led to a cross-linked network whereas at higher pH (6.1), conversions were too slow (around 10% after 350 min). (c) 2005 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据