期刊
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION
卷 56, 期 12, 页码 882-889出版社
WILEY-V C H VERLAG GMBH
DOI: 10.1002/maco.200503919
关键词
-
The reduction of emissions from power generation plants is a key part of the Kyoto Protocol. Reduced emissions per unit of power produced can be achieved via increased thermal efficiency and this can be achieved by increasing steam parameters (i.e. temperature and pressure). Increased steam parameters in turn leads to accelerated corrosion of boiler components. Biomass and solid waste fuels introduce a number of aggressive species into process environments that result in enhanced rates of boiler degradation. This paper reports on studies, both theoretical and experimental, of the corrosion behaviour of high-alloy steels and Ni-base alloys as well as coatings for use in high efficiency coal and/or biomass-and waste-fired power plants. Coatings produced within the SUNASPO project have been laboratory tested in gaseous atmospheres representative of coal combustion, biomass combustion and waste incineration. Laboratory tests were carried out mainly in the temperature range 500 degrees C to 800 degrees C. Initial results showed the poor performance of traditional uncoated low-alloy boiler steels P91 (9% Cr) and HCM12A (12% Cr), as well as the higher alloy steel, 17Cr/13Ni. Results show the beneficial effects of coatings containing Al, Si, Al + Si, Al + Ti and Al + B in reducing the rate of corrosive attack. In a combustion product gas containing 100 ppm HCl and 1000 ppm SO2, aluminizing affords corrosion resistance of low-alloy steels such as HCM12A and P91 similar to that of Alloy 800 over 1000 h of test. The presence of At inhibits internal, sometimes localized corrosion by promoting the formation of a protective surface oxide layer even at relatively low temperatures. The results of experiments in simulated coal; biomass and waste atmospheres are presented and discussed in terms of both corrosion kinetics and mechanisms of degradation.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据